Influence of Temperature on the Performance of LiNi1/3Co1/3Mn1/3O2 Prepared by High-Temperature Ball-Milling Method
Figure 5
(a) Charge-discharge curves of LiNi1/3Co1/3Mn1/3O2 powders prepared at various temperatures: (A) 700°C, (B) 750°C, (C) 800°C, and (D) 850°C at 0.1 C rate, (b) discharge curves at various currents, and (c) the dependence of specific capacity on current density.