Optimization of FCAW Parameters for Ferrite Content in 2205 DSS Welds Based on the Taguchi Design Method
| Number | I (A) | U (V) | S (cm/min) | T (degree) | Ferrite content | Desirability |
| 1 | 161.97 | 21.81 | 22.94 | 17.96 | 49.9999 | 1.000 | 2 | 185.79 | 20.25 | 25.55 | 7.37 | 50.0001 | 1.000 | 3 | 196.95 | 20.63 | 25.70 | 21.17 | 50 | 1.000 | 4 | 160.82 | 20.06 | 20.47 | 19.71 | 50 | 1.000 | 5 | 171.10 | 20.71 | 21.84 | 26.51 | 49.9999 | 1.000 | 6 | 174.18 | 20.74 | 22.34 | 25.93 | 50.0001 | 1.000 | 7 | 185.80 | 20.07 | 22.68 | 29.02 | 50.0001 | 1.000 | 8 | 174.37 | 20.32 | 22.32 | 22.17 | 50 | 1.000 | 9 | 161.08 | 25.98 | 25.28 | 29.58 | 49.9999 | 1.000 | 10 | 163.85 | 20.09 | 19.71 | 29.49 | 49.9999 | 1.000 |
|
|