Experimental Study on Variable-Amplitude Fatigue of Welded Cross Plate-Hollow Sphere Joints in Grid Structures
Table 2
The variable-amplitude fatigue test data of WCPHSJ under program block.
| Specimen label | (MPa) | (MPa) | (MPa) | | | Stress histogram of variable-amplitude fatigue |
| KQ-4-1 | 26.38 | 3.09 | 23.29 | 12.97 | 0.117 | | 28.37 | 3.29 | 25.08 | 44.35 | 0.116 | 29.36 | 3.39 | 25.97 | 19.24 | 0.115 | KQ-4-3 | 32.35 | 3.68 | 28.67 | 19.05 | 0.114 | | 28.37 | 3.29 | 25.08 | 107.37 | 0.116 | 26.38 | 3.09 | 23.29 | 124.87 | 0.117 | 25.38 | 2.99 | 22.39 | 27.89 | 0.118 | KQ-4-5 | 24.38 | 2.89 | 21.49 | 161.48 | 0.118 | | 32.35 | 3.68 | 28.67 | 12.11 | 0.114 | KQ-4-7 | 23.39 | 2.79 | 20.60 | 49.60 | 0.119 | | 24.38 | 2.89 | 21.49 | 50.30 | 0.118 | 25.38 | 2.99 | 22.39 | 10.68 | 0.118 | KQ-4-8 | 25.38 | 2.99 | 22.39 | 25.03 | 0.118 | | 26.38 | 3.09 | 23.29 | 53.07 | 0.117 | 28.37 | 3.29 | 25.08 | 44.35 | 0.116 | 29.36 | 3.39 | 25.97 | 21.56 | 0.115 | 34.83 | 3.93 | 30.90 | 14.04 | 0.113 | KQ-5-4 | 35.33 | 3.53 | 31.80 | 40.0 | 0.1 | | 37.02 | 3.70 | 33.32 | 18.41 | 0.1 | KQ-5-6 | 36.17 | 3.62 | 32.55 | 40.0 | 0.1 | | 37.86 | 3.79 | 34.07 | 40.0 | 0.1 | 39.54 | 3.95 | 35.59 | 40.0 | 0.1 | 41.22 | 4.12 | 37.10 | 40.0 | 0.1 | 42.90 | 4.29 | 38.61 | 13.03 | 0.1 | KQ-5-10 | 33.65 | 3.37 | 30.28 | 40.0 | 0.1 | | 35.33 | 3.53 | 31.80 | 25.05 | 0.1 | KQ-5-12 | 42.22 | 4.22 | 38.00 | 40.0 | 0.1 | | 44.44 | 4.44 | 40.00 | 40.0 | 0.1 | 46.67 | 4.67 | 42.00 | 24.75 | 0.1 | KQ-5-15 | 31.97 | 3.20 | 28.77 | 40.00 | 0.1 | | 33.65 | 3.37 | 30.28 | 40.00 | 0.1 | 35.33 | 3.53 | 31.80 | 40.00 | 0.1 | 38.70 | 3.87 | 34.83 | 8.24 | 0.1 | KQ-5-19 | 25.38 | 2.54 | 22.84 | 40.0 | 0.1 | | 26.38 | 2.64 | 23.74 | 40.0 | 0.1 | 28.37 | 2.84 | 25.53 | 40.0 | 0.1 | 29.36 | 2.94 | 26.42 | 14.05 | 0.1 | KQ-5-20 | 35.33 | 3.53 | 31.80 | 40.0 | 0.1 | | 37.02 | 3.70 | 33.32 | 40.0 | 0.1 | 38.70 | 3.87 | 34.83 | 40.0 | 0.1 | 40.38 | 4.04 | 36.34 | 40.0 | 0.1 | 42.33 | 4.23 | 38.10 | 52.87 | 0.1 | KQ-7-10 | 25.38 | 2.99 | 22.39 | 131.83 | 0.118 | | 24.38 | 2.89 | 21.49 | 161.48 | 0.118 | 32.35 | 3.68 | 28.67 | 178.96 | 0.114 | KQ-7-12 | 23.39 | 2.79 | 20.60 | 49.6 | 0.119 | | 24.38 | 2.89 | 21.49 | 50.3 | 0.118 | 25.38 | 2.99 | 22.39 | 40.6 | 0.118 | 26.38 | 3.09 | 23.29 | 39.94 | 0.117 |
|
|
Note. , axial load of fatigue specimens (kN); , width of crossed plate; , thickness of sphere; , nominal stress of fatigue specimens; , stress range; , stress ratio. |