Experimental Evidence of Precipitation of All 12 Variants in a Single β Grain in Titanium Alloys

Table 1

Euler angles and Burgers orientation relationship of all 12 variants.

Variants	Euler angle	Orientation relationship	3D orientations
BCC	(151.2, 33.8, 26.6)
V1	(38, 21.1, 49.3)
V2	(37.4, 19.6, 39.3)
V3	(171.4, 76.4, 39.3)
V4	(170.9, 76.1, 51)
V5	(51.1, 140.2, 36)
V6	(49.8, 140.4, 44.8)
V7	(130.7, 121.6, 43.2)
V8	(130.3, 121.8, 54.2)
V9	(47.1, 79.5, 33.5)
V10	(46.0, 79.2, 22.8)
V11	(107.5, 65.3, 2.7)
V12	(107.5, 66.5, 51.6)