Advances in Materials Science and Engineering / 2018 / Article / Tab 10 / Research Article
A Thermodynamics Study on the Tetrahydrofuran Effect in Exfoliated Graphite Nanoplatelets and Activated Carbon Mixtures at Temperatures between 293.15 and 308.15 K Table 10 Fitting parameters
A i and correlation coefficient
R 2 obtained for density
, speed of sound
c , refractive index
n D , isentropic compressibility
k S , and relaxation strength
r along with the absolute average percentage deviation (AAD%) for binary xGnP + THF mixtures.
a T (K)C (kg·m−3 )A 1 (kg·m−3 )A 2 (kg0 ·m0 )A 3 (kg−1 ·m3 )R 2 AAD% (kg·m−3 )293.15 0–100 887.61 0.0075589 −0.0000040 0.99423 0.002 298.15 0–100 882.17 0.0070750 0.0000027 0.99438 0.002 303.15 0–100 876.65 0.0086321 −0.0000080 0.98620 0.003 308.15 0–100 871.14 0.0088200 −0.0000100 0.99598 0.002 T (K)C (kg·m−3 )A 1 (kg0 ·m−1 ·s)A 2 (kg·m−4 ·s)A 3 (kg2 ·m−7 ·s)R 2 AAD% c (m·s−1 )293.15 0–100 1303.65 −0.002848 0.000023 0.99669 0.001 298.15 0–100 1279.38 0.003270 −0.000025 0.99509 0.001 303.15 0–100 1255.24 0.004354 −0.000035 0.98499 0.002 308.15 0–100 1231.10 0.005780 −0.000042 0.98843 0.001 T (K)C (kg·m−3 )A 1 A 2 ·105 A 3 ·107 R 2 AAD% n D 293.15 0–100 1.40735 −0.000032012 0.000000353 0.98442 0.086 298.15 0–100 1.40468 −0.000032420 0.000000351 0.98895 0.084 303.15 0–100 1.40203 −0.000035411 0.000000388 0.98336 0.119 308.15 0–100 1.39935 −0.000028093 0.000000320 0.97351 0.092 T (K)C (kg·m−3 )A 1 (10−10 ·kg0 ·m2 ·N−1 )A 2 (10−9 ·kg−1 ·m5 ·N−1 )A 3 (10−9 ·kg−2 ·m8 ·N−1 )R 2 AAD% k S (10−10 ·m2 ·N−1 )293.15 0–100 6.6291139 −0.000273 −0.000002 0.991057 0.002 298.15 0–100 6.9255086 −0.000910 0.000002 0.996994 0.003 303.15 0–100 7.2397718 −0.001216 0.000005 0.991389 0.003 308.15 0–100 7.5739754 −0.001478 0.000006 0.995453 0.002 T (K)C (kg·m−3 )A 1 (kg0 ·m0 )A 2 (kg−1 ·m3 )A 3 (kg−2 ·m−6 )R 2 AAD% r 293.15 0–100 0.33613 0.000002848 −0.000000023 0.99669 0.001 298.15 0–100 0.36062 −0.000003270 0.000000025 0.99508 0.001 303.15 0–100 0.38453 −0.000004354 0.000000035 0.98499 0.001 308.15 0–100 0.40797 −0.000005780 0.000000042 0.98843 0.002
a A i and
R 2 were obtained from (
2 ).