Comparative Study of the Mechanical and Water Absorption Behaviour of Basalt Fiber Reinforced Polymer Matrix Composites with Different Epoxies as Matrix for Biomedical Applications
Table 2
Properties of different epoxy-hardener combinations.
Laminate
Epoxy-hardener combination
Epoxy density at 25°C in g/cc (ISO 1675)
Hardener density at 25°C in g/cc (ISO 1675)
Epoxy viscosity at 25°C in MPa s (ISO 12058-1)
Hardener viscosity at 25°C in MPa s (ISO 12058-1)
Curing conditions used
L
1
Lapox L12-hardener K6
1.120
0.954
9000–12000
5000–8000
80
0
C for 1-2 hrs
L
2
Araldite LY1564-Aradur 22962
1.1 to 1.2
0.89–0.90
1200–1400
5–20
80
0
C for 1 hr
L
3
Araldite LY556-Aradur HY951
1.1 to 1.2
0.980
1350–2000
10–20
Room temperature (25°C for 24 to 48 hrs)