Effects of Annealing and Deformation on Sagging Resistance of a Hot-Rolled, Four-Layered Al Alloy Clad Sheet
Table 1
Chemical compositions of 4343/3003/6111/3003 (mass fraction, %).
| Material | Wt. (mass fraction, %) | Si | Fe | Cu | Mn | Mg | Zn | Ti | Al |
| 4343 | 7.8–8.2 | 0.15–0.30 | 0.05 | 0.05 | 0.03 | – | – | Bal. | 3003 | 0.6 | 0.7 | 0.05–0.20 | 1.0–1.5 | – | 0.10 | – | Bal. | 6111 | 0.7–1.1 | <0.4 | 0.5–1.0 | 0.10–0.45 | 0.50–1.0 | <0.15 | <0.10 | Bal. |
|
|