Identifying the Thermal Storage Stability of Polymer-Modified Asphalt with Carbon Nanotubes Based on Its Macroperformance and Micromorphology
Table 1
Technical characteristics of A70# asphalt binders.
| | Index | Test result | Technical requirement |
| | 25°C, 100 g, 5s, penetration (0.1 mm) | 63 | 60∼80 | | Penetration index | −1.45 | −1.5∼+1.0 | | Softening point (°C) | 46.2 | | | 60°C, dynamic viscosity (Pa.s) | 248 | | | 10°C, 5 cm/min, ductility (cm) | 22.51 | | | Wax content (%) | 2.18 | <2.2 | | Quality change (%) | 0.05 | | RTFOT | 25°C, residual penetration ratio (%) | 73.85 | | | 10°C, residual ductility (cm) | 9 | |
|
|