Spheroidization and Coarsening of Eutectic Si Particles in Al-Si-Based Alloys

Figure 21

Macrocracking observed in 319 alloy after solutionizing at 550°C (about 40°C above the melting point of Al₂Cu); note the deflection in the last bar (sold black line) under gravity compared to the centre line (broken line) [30].