Spheroidization and Coarsening of Eutectic Si Particles in Al-Si-Based Alloys
Table 2
Characteristics of Si particles in 319 alloy (coded A) at different conditions (nonmodified).
| Condition | Average particle area (μm2) | Average particle length (μm) | Particle roundness (%) | Particle aspect ratio | Density (particles/μm2) | μ | σ | μ | Σ | Μ | σ | μ | σ | μ |
| As-cast | 48.99 | 18.19 | 13.26 | 6.89 | 67.10 | 32.36 | 2.55 | 1.52 | 2365 | 8 h@510°C | 86.55 | 49.69 | 15.63 | 13.04 | 60.87 | 31.94 | 2.48 | 1.42 | 1762 | 24 h@510°C | 75.86 | 52.51 | 14.66 | 13.47 | 60.23 | 29.49 | 2.42 | 1.34 | 1455 |
|
|
Average value; standard deviation. |