Spheroidization and Coarsening of Eutectic Si Particles in Al-Si-Based Alloys

Table 4

Characteristics of Si particles in 356 alloy at different conditions (nonmodified (coded B) and Sr-modified (coded BS) conditions).

Alloy code	Solutionizing time (h)	Particle area (μm^2)	Sphericity (%)	Roundness (%)	Aspect ratio	Density (particles/mm^2)
B	As-cast	μ = 14.30	μ = 41.60	μ = 36.30	μ = 2.44	μ = 27000
		σ = 11.70	σ = 22.70	σ = 19.00	σ = 1.53
	8	μ = 21.50	μ = 72.50	μ = 46.30	μ = 1.83	μ = 1200
		σ = 17.30	σ = 18.00	σ = 17.70	σ = 1.53
	24	μ = 27.50	μ = 42.50	μ = 50.30	μ = 1.63	μ = 4200
		σ = 19.30	σ = 18.00	σ = 17.70	σ = 1.50
	50	μ = 33.70	μ = 72.90	μ = 56.40	μ = 1.73	μ = 7000
		σ = 22.80	σ = 16.30	σ = 16.90	σ = 0.81
	100	μ = 48.00	μ = 78.20	μ = 64.90	μ = 1.78	μ = 3500
		σ = 48.70	σ = 18.10	σ = 24.20	σ = 0.98
	200	μ = 69.10	μ = 79.20	μ = 63.80	μ = 1.79	μ = 2700
		σ = 44.10	σ = 18.30	σ = 24.10	σ = 1.12
	400	μ = 77.60	μ = 81.00	μ = 66.80	μ = 1.71	μ = 3100
		σ = 63.70	σ = 18.80	σ = 22.70	σ = 1.15
	1200	μ = 85.60	μ = 87.00	μ = 69.80	μ = 1.51	μ = 3900
		σ = 45.70	σ = 15.80	σ = 22.70	σ = 1.15
BS	As-cast	μ = 6.82	μ = 54.90	μ = 46.30	μ = 1.88	μ = 44000
		σ = 6.05	σ = 23.20	σ = 17.50	σ = 0.81
	8	μ = 15.30	μ = 75.50	μ = 62.20	μ = 1.53	μ = 17000
		σ = 11.60	σ = 17.40	σ = 15.20	σ = 0.56
	24	μ = 21.30	μ = 76.50	μ = 63.20	μ = 1.00	μ = 4350
		σ = 15.60	σ = 17.40	σ = 14.70	σ = 0.56
	50	μ = 28.40	μ = 78.30	μ = 64.80	μ = 1.54	μ = 7000
		σ = 20.90	σ = 15.2	σ = 14.70	σ = 0.90
	100	μ = 42.60	μ = 82.70	μ = 67.50	μ = 1.53	μ = 5100
		σ = 40.30	σ = 15.60	σ = 17.80	σ = 0.74
	200	μ = 60.00	μ = 85.80	μ = 69.90	μ = 1.45	μ = 3800
		σ = 43.70	σ = 14.40	σ = 17.10	σ = 0.58
	400	μ = 77.90	μ = 82.60	μ = 69.00	μ = 1.56	μ = 4100
		σ = 65.00	σ = 18.00	σ = 21.00	σ = 0.93
	1200	μ = 93.90	μ = 86.60	μ = 77.00	μ = 1.35	μ = 3800
		σ = 50.00	σ = 15.00	σ = 18.00	σ = 0.83