Spheroidization and Coarsening of Eutectic Si Particles in Al-Si-Based Alloys

Table 5

Characteristics of Si particles in 413 alloy at different conditions (nonmodified (coded C) and Sr-modified (coded CS) conditions).

Alloy code	Solutionizing time (h)	Particle area (μm^2)	Sphericity (%)	Roundness (%)	Aspect ratio	Density (particles/mm^2)
C	As-cast	μ = 19.00	μ = 44.00	μ = 36.60	μ = 3.87	Μ = 18000
		σ = 19.60	σ = 23.10	σ = 16.70	σ = 1.08
	8	μ = 17.30	μ = 66.90	μ = 50.00	μ = 2.31	Μ = 9800
		σ = 16.00	σ = 25.10	σ = 22.10	σ = 1.27
	24	μ = 14.90	μ = 74.20	μ = 51.70	μ = 2.10	Μ = 8200
		σ = 14.80	σ = 20.10	σ = 19.20	σ = 1.03
	50	μ = 27.60	μ = 73.20	μ = 52.50	μ = 2.02	Μ = 6300
		σ = 19.40	σ = 19.80	σ = 19.00	σ = 0.95
	100	μ = 42.00	μ = 73.50	μ = 52.90	μ = 2.01	Μ = 4400
		σ = 29.40	σ = 19.00	σ = 18.40	σ = 0.91
	200	μ = 61.50	μ = 74.10	μ = 54.60	μ = 1.99	Μ = 3400
		σ = 36.80	σ = 18.30	σ = 19.10	σ = 0.90
	400	μ = 72.50	μ = 76.10	μ = 55.2	μ = 1.82	Μ = 2800
		σ = 35.6	σ = 17.40	σ = 17.10	σ = 0.70
	1200	μ = 91.50	μ = 78.10	μ = 60.40	μ = 1.52	Μ = 1900
		σ = 31.2	σ = 16.30	σ = 17.30	σ = 0.70
CS	As-cast	μ = 3.59	μ = 52.70	μ = 46.50	μ = 1.96	μ = 34000
		σ = 6.28	σ = 23.90	σ = 20.90	σ = 0.78
	8	μ = 6.11	μ = 72.20	μ = 57.00	μ = 1.69	μ = 18000
		σ = 6.59	σ = 18.40	σ = 15.90	σ = 0.60
	24	μ = 10.50	μ = 75.60	μ = 61.50	μ = 1.56	μ = 10000
		σ = 9.99	σ = 18.40	σ = 15.80	σ = 0.56
	50	μ = 16.50	μ = 79.30	μ = 62.30	μ = 1.56	Μ = 7500
		σ = 16.00	σ = 18.20	σ = 16.20	σ = 0.53
	100	μ = 36.20	μ = 79.20	μ = 63.40	μ = 1.57	Μ = 5400
		σ = 24.00	σ = 17.70	σ = 16.50	σ = 0.64
	200	μ = 47.30	μ = 80.30	μ = 64.20	μ = 1.5	Μ = 4400
		σ = 28.10	σ = 16.10	σ = 14.90	σ = 0.467
	400	μ = 58.30	μ = 82.40	μ = 66.30	μ = 1.5	Μ = 3500
		σ = 21.2	σ = 16.4	σ = 13.90	σ = 0.467
	1200	μ = 69.30	μ = 85.30	μ = 71.40	μ = 1.5	Μ = 3000
		σ = 22.10	σ = 15.10	σ = 14.4	σ = 0.467