Polyvinyl Alcohol Fiber Length Optimization for High Ductility Cementitious Composites with Different Compressive Strength Grades

<div>Effect of the fiber length on the bridging stress and complementary energy with various fiber/matrix interfacial bonding strengths. (a) Fiber bridging stress <span class="nowrap"><svg height="9.4347pt" id="M43" style="vertical-align:-3.29111pt" version="1.1" viewbox="-0.0498162 -6.14359 11.8314 9.4347" width="11.8314pt" xmlns="http://www.w3.org/2000/svg" xmlns:xlink="http://www.w3.org/1999/xlink"><g transform="matrix(.013,0,0,-0.013,0,0)"><path d="M548 455L523 469C505 448 490 439 461 439C416 439 374 447 316 447C144 447 23 310 23 161C23 47 89 -12 179 -12C312 -12 429 106 429 244C429 303 419 344 368 386L371 388C404 383 440 378 474 378C507 378 530 411 548 455ZM350 274C350 191 308 25 198 25C144 25 108 75 108 157C108 264 170 395 276 395C296 395 320 384 333 360C347 334 350 316 350 274Z"></path></g><g transform="matrix(.0091,0,0,-0.0091,6.76,3.132)"><path d="M245 635C92 635 37 457 37 312C37 149 91 -12 244 -12C395 -12 449 166 449 312C449 469 395 635 245 635ZM243 598C332 598 358 454 358 312C358 173 334 26 245 26C158 26 128 174 128 313S152 598 243 598Z"></path></g></svg>.</span> (b) Complementary energy <span class="nowrap"><svg height="15.3797pt" id="M44" style="vertical-align:-3.9436pt" version="1.1" viewbox="-0.0498162 -11.4361 10.0137 15.3797" width="10.0137pt" xmlns="http://www.w3.org/2000/svg" xmlns:xlink="http://www.w3.org/1999/xlink"><g transform="matrix(.013,0,0,-0.013,0,0)"><path d="M429 650H175L169 622C251 614 259 612 244 532L174 152C163 91 152 37 135 -6C109 -72 67 -101 23 -113L33 -144C45 -143 73 -134 102 -119C186 -76 229 -1 254 133L327 532C341 609 347 613 423 622L429 650Z"></path></g><g transform="matrix(.0091,0,0,-0.0091,5.879,-5.741)"><path d="M310 541L304 571C290 586 211 619 185 610L80 76L131 52L310 541Z"></path></g><g transform="matrix(.0091,0,0,-0.0091,5.031,3.784)"><path d="M460 334C460 396 434 451 378 451C330 451 241 408 148 300H146L237 679C241 697 241 710 232 710C213 710 153 684 67 675L66 646H95C141 646 145 642 134 595L39 170C23 97 31 54 46 33C64 8 100 -12 137 -12C178 -12 234 3 298 43C391 101 460 222 460 334ZM371 320C371 204 316 89 248 51C230 41 208 37 192 37C143 37 102 72 119 166C124 194 129 215 135 235C202 323 298 392 335 392C353 392 371 372 371 320Z"></path></g></svg>.</span></div>

Advances in Materials Science and Engineering

fig7

Figure 7

Figure 7: Polyvinyl Alcohol Fiber Length Optimization for High Ductility Cementitious Composites with Different Compressive Strength Grades 