Review Article
Mechanical Properties of Titanium Diboride Particles Reinforced Aluminum Alloy Matrix Composites: A Comprehensive Review
Table 3
Superior mechanical properties of titanium diboride based aluminum matrix composites.
| MMCs | Manufacturing process | Macrohardness (BHN) | Microhardness (HV) | UTS (MPa) | YS (MPa) | Reference |
| AA7050/6 wt% TiB2 | In situ casting technique | — | — | 746 | 701 | [25] | AA6061/12 wt% TiB2 | Exothermic reaction process | 88.6 | — | 173.6 | 94.2 | [34] | Al/7 wt% TiB2 | Salt-metal reaction route | 30 | — | 136.6 | — | [35] | A356/8.37 vol% TiB2 | In situ reaction process | — | — | 258.5 | 217.6 | [36] | AA2219/10 wt% TiB2 | In situ casting technique | — | 96 | 234 | 205 | [37] | AA6063/13.12 wt% TiB2 | In situ casting | — | 59.25 | 140.9 | — | [38] | AA6061/10 wt% TiB2 | High energy stir casting | — | 73.93 | 171 | — | [39] | AA7075/9 wt% TiB2 | In situ method | — | 128 | 285 | — | [40, 85] | AA6063/10 wt% TiB2 | In situ casting route | — | 110 | — | — | [41, 73] | A356/12.5 wt% TiB2 | Exothermic reaction process | — | — | 382 | 324 | [42] | AA6061/12 wt% TiB2 | Stir casting | — | 72.46 | 137.86 | — | [43] | Al-6Cu-0.2Mg-1Mn/5 wt% TiB2 | In situ casting | — | 84 | — | — | [44] | AA6061/10 wt% TiB2 | Melt stirring process | — | 58 | 195 | — | [45] | AA2219/10 wt% TiB2 | In situ reaction method | — | — | 426.97 | 301.75 | [47] | LM/7.5 wt% TiB2 | Mixed salts method | — | — | 202 | 164 | [48] | A356/0.5 wt% TiB2 | Stir casting | — | 118 | — | — | [50] | AA356/7.8 vol% TiB2 | In situ casting | — | — | 382 | 328 | [51] | AA6061/7 wt% TiB2 | Mixed salt route | — | 47 | 145 | — | [52] | AA6061/9 wt% TiB2 | Exothermic reaction process | — | 123 | — | — | [54] | Al-4.5%Cu-3%C/15 vol% TiB2 | In situ method | — | — | 257.6 | — | [55] | Al(CP)/20 vol% TiB2 | Powder metallurgy | —- | — | 191 | 115 | [56] | LM25/7.5 wt% TiB2 | In situ reaction casting | 81 | — | 202 | 164 | [57] | Al-4Cu/10 wt% TiB2 | Liquid state in situ casting | — | 138 | — | — | [58] | AA6061/12 wt% TiB2 | Stir casting | — | 77.93 | 140 | — | [60] | AA6061/2.5 wt% TiB2/10% SiC | Liquid state stir casting | — | 71.46 | — | — | [64] | AA6061/10 wt% TiB2 | In situ method | — | 74.83 | 165.74 | — | [65] | Al(CP)/wt% TiB2 | In situ method | — | — | 180 | 96 | [66] | AA7178/9 wt% TiB2 | In situ casting route | — | 94 | 211 | — | [67] | Al-7Si/13.12 wt% TiB2 | In situ reaction process | — | 102 | 209 | 152 | [69] | AA6061/20 wt% TiB2/2Gr | Stir casting route | — | 91.4 | 170 | — | [72] | AA6061/2.5 wt% TiB2/10 wt% SiC | Stir casting | — | 75 | — | — | [76] | AA6061/10 wt% TiB2/2 wt% gr | Stir casting | — | 79.04 | — | — | [77] | AA2219—6 wt%TiB2/ZrB2 | In situ casting | — | 155.6 | — | — | [79] | A356/2.5 wt% TiB2 | In situ technique | — | 92 | — | — | [81, 84] | AA6061/14 wt% TiB2 | In situ technique | — | 128 | 334 | — | [83] | AA2009/8 wt% TiB2 (solution temperature 520°C) | In situ method | — | — | 538 | 364 | [86] | AA2024/7 wt% TiB2 | Stir casting | — | 116 | — | — | [87] | AA7075/12 wt% TiB2 | In situ technique | — | 141 | 287.95 | — | [88] |
|
|