Effect of Cyclic Cryogenic Treatment on Wear Resistance, Impact Toughness, and Microstructure of 42CrMo Steel and Its Optimization
Table 4
Wear test results of CHT and CT specimens.
| Exp. no. | Wear loss (mg) | Wear rate (10−3 mg m−1) | Relative wear rate (%) |
| CHT | 46.3 | 34.1152 | 1.00 | CT1 | 43.6 | 32.1257 | 0.94 | CT2 | 45.7 | 33.6731 | 0.99 | CT3 | 42.6 | 31.3889 | 0.92 | CT4 | 40.4 | 29.7679 | 0.87 | CT5 | 38.6 | 28.4416 | 0.83 | CT6 | 41.2 | 30.3573 | 0.89 | CT7 | 43.2 | 31.8310 | 0.93 | CT8 | 40.1 | 29.5468 | 0.87 | CT9 | 37.3 | 27.4837 | 0.81 |
|
|