Effect of Dispersoids and Intermetallics on Hardening the Al-Si-Cu-Mg Cast Alloys
Figure 8
Bright field electron micrographs showing the progress in the size and distribution of the precipitated second phase during aging at 190ºC. (a) 2 h, (b) 200 h, (c) 1000 h, (d) dislocation/particle imteractions in condition (c), note the high dislocation density, (e) dislocation density in alloy A after solutionizing treatment, note the size of the preciptated particles in the white area, and (f) EDS spectrum corresponding to square area in (c) revealing Al and Cu peaks.