Effect of Dispersoids and Intermetallics on Hardening the Al-Si-Cu-Mg Cast Alloys

<table class="table-group" id="tab3"><tr><td><table class="table"><tr><td class="thead-hr" colspan="4"><hr/></td></tr><tr class="thead"><td class="align_left">Parameter-</td><td class="align_center">UTS (MPa)</td><td class="align_center">YS (MPa)</td><td class="align_center">%El</td></tr><tr><td class="thead-hr" colspan="4"><hr/></td></tr><tr><td class="align_left">Value</td><td class="align_center">235</td><td class="align_center">154</td><td class="align_center">1.6</td></tr><tr class="table-tr"><td colspan="4"><hr class="tbody-hr"/></td></tr></table></td></tr></table>

<div>Tensile properties of alloy A in the as-cast condition.</div>

Advances in Materials Science and Engineering

tab3

Table 3

Table 3: Effect of Dispersoids and Intermetallics on Hardening the Al-Si-Cu-Mg Cast Alloys 