Effect of Fiber Content on Mechanical Properties and Microstructural Characteristics of Alkali Resistant Glass Fiber Reinforced Concrete
Table 7
EDS quantitative analyses ARGFRC EDS-FC0 and EDS-FC0.8.
| Specimen | Element | Element concentration | Strength correction | Weight percentage | Weight percentage sigma |
| EDS-FC0 | C K | 45.92 | 0.3551 | 23.94 | 0.76 | O K | 107.67 | 0.3339 | 59.72 | 0.62 | Mg K | 1.99 | 0.5671 | 0.65 | 0.03 | Al K | 1.89 | 0.6912 | 0.51 | 0.02 | Si K | 9.87 | 0.7953 | 2.30 | 0.04 | K K | 0.64 | 0.9966 | 0.12 | 0.02 | Ca K | 63.43 | 0.9206 | 12.76 | 0.15 | Total | | | 100.00 | |
| EDS-FC0.8 | C K | 17.03 | 0.2986 | 21.91 | 1.23 | O K | 46.65 | 0.3205 | 55.93 | 0.93 | Mg K | 3.93 | 0.5842 | 2.58 | 0.08 | Al K | 3.85 | 0.6862 | 2.15 | 0.06 | Si K | 6.41 | 0.7741 | 3.18 | 0.08 | K K | 0.59 | 0.9915 | 0.23 | 0.03 | Ca K | 33.50 | 0.9188 | 14.01 | 0.25 | Total | | | 100.00 | |
|
|