Effect of Nanomaterials on Tribological and Mechanical Properties of Polymer Nanocomposite Materials
Table 1
Tensile testing results of different nanocomposites.
| Nanocomposites | Young’s modulus (GPa) | Tensile strength (MPa) | Ref. |
| Neat DGEBA epoxy | 2.71 ± 0.11 | 72.06 ± 1.37 | [53] | 2 wt.% Na+/DGEBA epoxy | 2.79 ± 0.07 | 68.04 ± 4 | [53] | 5 wt.% Na+/DGEBA epoxy | 2.92 ± 0.17 | 57.2 ± 2.22 | [53] | 10 wt.% Na+/DGEBA epoxy | 3.44 ± 0.29 | 57.68 ± 3.69 | [53] | 2 wt.% C30B/DGEBA epoxy | 3.11 ± 0.09 | 62.19 ± 2.56 | [53] | 5 wt.% C30B/DGEBA epoxy | 3.10 ± 0.08 | 58.35 ± 5.87 | [53] | 10 wt.% C30B/DGEBA epoxy | 3.12 ± 0.23 | 57.31 ± 6.97 | [53] | 2 wt.% NI.30E/DGEBA epoxy | 2.68 ± 0.26 | 64.58 ± 6.56 | [53] | 5 wt.% NI.30E/DGEBA epoxy | 2.82 ± 0.12 | 59.94 ± 9.01 | [53] | 10 wt.% NI.30E/DGEBA epoxy | 3.04 ± 0.11 | 58.23 ± 4.39 | [53] | 2 wt.% CPC/DGEBA epoxy | 2.57 ± 0.15 | 49.03 ± 2.72 | [53] | 5 wt.% CPC/DGEBA epoxy | 2.79 ± 0.08 | 50.14 ± 2.80 | [53] | Neat DGEBA epoxy/carbon fiber | 46.5 ± 0.6 | 848 ± 18.2 | [54] | 5 wt.% CSCNT/DGEBA epoxy/carbon fiber | 47.9 ± 0.7 | 844 ± 5.3 | [54] | 10 wt.% CSCNT/DGEBA epoxy/carbon fiber | 48.3 ± 1.7 | 850 ± 40.0 | [54] | Neat DGEBA epoxy/basalt fiber | 27.65 ± 0.41 | 584.7 ± 10.3 | [55] | 0.5 wt.% raw MWCNT/DGEBA epoxy/basalt fiber | 27.44 ± 0.76 | 564.0 ± 31.0 | [55] | 0.5 wt.% o-MWCNT(acid treated)/DGEBA epoxy/basalt fiber | 30.41 ± 1.31 | 635.7 ± 33.8 | [55] | 0.5 wt.% PGE-MWCNT(phenyl glycidyl ether added)/DGEBA epoxy/basalt fiber | 29.92 ± 0.83 | 608.8 ± 20.0 | [55] | 1.5 wt.% raw MWCNT/DGEBA epoxy/basalt fiber | 28.53 ± 1.18 | 504.0 ± 42.0 | [55] | 1.5 wt.% o-MWCNT/DGEBA epoxy/basalt fiber | 36.4 ± 0.97 | 627.7 ± 25.5 | [55] | 1.5 wt.% PGE-MWCNT/DGEBA epoxy/basalt fiber | 34.90 ± 0.77 | 615.1 ± 19.7 | [55] | 1.25 wt.% attapulgite clay(ATT)/DGEBA epoxy/basalt fiber | 29.85 ± 1.03 | 530.9 ± 43.4 | [55] | 2.5 wt.% ATT/DGEBA epoxy/basalt fiber | 28.06 ± 2.62 | 465.4 ± 94.5 | [55] | Neat poly(ethylene terephthalate) (PET) polyclear-machine direction (MD) | 2.0 ± 0.1 | 62.6 ± 0.7 | [56] | 1 wt.% MWCNT/PET-MD | 2.25 ± 0.07 | 66.9 ± 0.8 | [56] | 2 wt.% MWCNT/PET- MD | 2.57 ± 0.08 | 72.5 ± 0.2 | [56] | 4 wt.% MWCNT/PET- MD | 2.80 ± 0.32 | 89.1 ± 4.2 | [56] | Neat PET-transverse direction (TD) | 1.93 ± 0.01 | 59.0 ± 1.2 | [56] | 1 wt.% MWCNT/PET- TD | 2.13 ± 0.08 | 65.4 ± 0.7 | [56] | 2 wt.% MWCNT/PET- TD | 2.34 ± 0.20 | 68.2 ± 1.0 | [56] | 4 wt.% MWCNT/PET- TD | 2.75 ± 0.08 | 76.5 ± 0.8 | [56] | Neat DGEBA epoxy | 3062 ± 47 | 80.3 ± 0.8 | [57] | 10 wt.% Somasif M-100/DGEBA epoxy | 4719 ± 130 | 51.5 ± 1.4 | [57] |
|
|