Effect of Nanomaterials on Tribological and Mechanical Properties of Polymer Nanocomposite Materials
Table 4
ILSS property for various nanofillers.
| Nanofiller | Dispersion status | ILSS property comments | Ref. |
| Cloisite 30B | 1 wt.%, 3 wt.% | Greater enhancement attained for 3 wt.% Cloisite 30B | [99] | RXG 7000 | 3 wt.% | Nano-silica | 10 wt.%, 20 wt.% | 12% greater reduction for 20 wt.% nano-silica-modified epoxy laminate | [89] | Nano-SiO2 | Unsized composites | 9% enhancement for unmodified sizing composites; 14% enhancement for nano-SiO2-modified sizing composites | [96] | Unmodified sizing composites | Nano-SiO2-modified sizing composites |
| MWNT | 0.5 wt.% unfunctionalized MWNT-modified epoxy | 41% increase than neat epoxy/glass fiber composites | [97] | 0.5 wt.% amino-functionalized MWNT-modified epoxy | 61% increase than neat epoxy/glass fiber composites |
| Na + MMT clay | 1, 3, 6, and 10% wt. of unmodified montmorillonite | ILSS reduced slightly and greater reduction for OMMT clay particles | [88] | 1, 3, 6, and 10% wt. of organo-modified montmorillonite |
|
|