Experimental Study on Crushing Characteristics of Lignite under Different Load Conditions
Table 2
Relevant parameters of point-load test and calculation results of strength index.
| Numbered | W (mm) | D (mm) | P (kN) | Is (MPa) | F/1 | Is50 (MPa) |
| 1 | 85 | 60 | 1.49 | 0.25 | 1.22 | 0.30 | 2 | 96 | 54 | 1.86 | 0.31 | 1.22 | 0.38 | 3 | 104 | 90 | 2.06 | 0.18 | 1.41 | 0.25 | 4 | 82 | 75 | 1.88 | 0.26 | 1.27 | 0.33 | 5 | 83 | 71 | 1.56 | 0.22 | 1.26 | 0.28 | 6 | 117 | 95 | 2.09 | 0.16 | 1.46 | 0.23 | 7 | 96 | 55 | 2.04 | 0.33 | 1.23 | 0.40 | 8 | 98 | 50 | 1.38 | 0.24 | 1.21 | 0.29 | 9 | 102 | 82 | 3.51 | 0.36 | 1.36 | 0.49 | 10 | 65 | 55 | 0.44 | 0.10 | 1.13 | 0.11 | 11 | 74 | 52 | 0.92 | 0.20 | 1.14 | 0.23 | 12 | 140 | 55 | 1.77 | 0.20 | 1.33 | 0.26 | 13 | 81 | 62 | 0.94 | 0.16 | 1.22 | 0.19 | 14 | 83 | 65 | 1.49 | 0.23 | 1.24 | 0.28 | 15 | 104 | 55 | 1.28 | 0.19 | 1.25 | 0.24 | 16 | 109 | 57 | 1.42 | 0.19 | 1.28 | 0.24 | 17 | 132 | 65 | 2.64 | 0.27 | 1.36 | 0.37 | 18 | 75 | 60 | 1.56 | 0.29 | 1.19 | 0.35 | 19 | 109 | 52 | 1.62 | 0.24 | 1.25 | 0.30 | 20 | 109 | 65 | 2.85 | 0.36 | 1.30 | 0.46 | 21 | 113 | 56 | 1.84 | 0.24 | 1.28 | 0.31 | 22 | 108 | 66 | 2.49 | 0.30 | 1.31 | 0.39 | 23 | 67 | 50 | 1.29 | 0.32 | 1.11 | 0.36 | 24 | 83 | 55 | 1.67 | 0.34 | 1.16 | 0.40 | 25 | 73 | 55 | 1.52 | 0.32 | 1.15 | 0.37 | 26 | 75 | 70 | 2.2 | 0.37 | 1.22 | 0.45 | 27 | 68 | 55 | 1.57 | 0.36 | 1.13 | 0.41 |
|
|
Average value Is50 = 0.32 MPa after removing the minimum and maximum data.
|