Research Article
[Retracted] Optimization and Mechanical Properties of TiO2 Reinforced AA 7150 Composites Using Response Surface Methodology
Table 4
Experimental results, levels, and outputs.
| Experimental run | Levels | Factors | Responses | A(°C) | B(rpm) | C(min) | A(°C) | B(rpm) | C(min) | YS | UTS | EM | El | IM |
| 1 | −1 | −1 | −1 | 550 | 450 | 10 | 501 | 581 | 82.6 | 8.76 | 4.21 | 2 | 0 | 0 | −1.68 | 550 | 450 | 10 | 525 | 642 | 90.1 | 7.84 | 5.31 | 3 | 0 | 0 | 0 | 550 | 450 | 10 | 529 | 689 | 91.4 | 7.51 | 5.74 | 4 | 0 | 0 | 0 | 550 | 550 | 15 | 546 | 635 | 86.5 | 7.52 | 5.46 | 5 | 0 | 0 | 0 | 550 | 550 | 15 | 575 | 719 | 95.3 | 6.79 | 6.41 | 6 | 0 | 1.68 | 0 | 550 | 550 | 15 | 588 | 682 | 98.2 | 6.43 | 6.86 | 7 | 1 | 1 | −1 | 550 | 650 | 20 | 522 | 600 | 79.4 | 7.82 | 4.86 | 8 | −1 | 1 | 1 | 550 | 650 | 20 | 559 | 622 | 88.6 | 7.99 | 5.51 | 9 | −1.68 | 0 | 0 | 550 | 650 | 20 | 574 | 637 | 92.1 | 6.62 | 5.90 | 10 | 1.68 | 0 | 0 | 650 | 450 | 15 | 530 | 634 | 87.3 | 8.55 | 5.17 | 11 | 0 | 0 | 0 | 650 | 450 | 15 | 558 | 715 | 92.3 | 7.24 | 5.86 | 12 | 1 | −1 | 1 | 650 | 450 | 15 | 564 | 734 | 98.5 | 7.12 | 6.13 | 13 | 0 | −1.68 | 0 | 650 | 550 | 20 | 579 | 672 | 92.6 | 8.08 | 5.78 | 14 | −1 | −1 | 1 | 650 | 550 | 20 | 601 | 745 | 96.5 | 7.34 | 6.84 | 15 | 0 | 0 | 0 | 650 | 550 | 20 | 629 | 771 | 102.3 | 6.09 | 7.15 | 16 | 1 | 1 | 1 | 650 | 650 | 10 | 561 | 628 | 86.7 | 8.47 | 5.00 | 17 | 0 | 0 | 1.68 | 650 | 650 | 10 | 582 | 665 | 91.2 | 7.12 | 5.66 | 18 | −1 | 1 | −1 | 650 | 650 | 10 | 618 | 692 | 93.2 | 6.83 | 6.16 | 19 | 1 | −1 | −1 | 750 | 450 | 20 | 524 | 600 | 84.5 | 8.17 | 4.24 | 20 | 0 | 0 | 0 | 750 | 450 | 20 | 531 | 657 | 86.8 | 6.94 | 4.87 |
|
|