Assessment of Rotational Speed and Plunge Rate on Lap Shear Strength of FSSW Joints of AA7075/Mild Steel
Table 4
Influence of speed of tool rotation on the macrograph.
| Speed of tool rotation | Macrostructure | Observation |
| 800 | | TSFL = 6.12 kN; HH = 1.52 mm; | HW = 1.25 mm; HID = 2.14 mm; | ABVHTP = 156.23 mm3 | 850 | | TSFL = 7.18 kN; HH = 1.48 mm; | HW = 1.28 mm; HID = 2.45 mm; | ABVHTP = 161.21 mm3 | 900 | | TSFL = 9.46 kN; HH = 1.44 mm; | HW = 1.35 mm; HID = 2.95 mm; | ABVHTP = 165.02 mm3 | 950 | | TSFL = 8.12 kN; HH = 1.51 mm; | HW = 1.30 mm; HID = 2.88 mm; | ABVHTP = 158.52 mm3 | 1000 | | TSFL = 7.21 kN; HH = 1.63 mm; | HW = 1.25 mm; HID = 2.65 mm; | ABVHTP = 155.23 mm3 |
|
|