Assessment of Rotational Speed and Plunge Rate on Lap Shear Strength of FSSW Joints of AA7075/Mild Steel
Table 5
Influence of the rate of plunge on TSFL of dissimilar FSSW joints.
| Rate of plunge (mm/min) | Macrograph | Observation |
| 2 | | TSFL = 7.06 kN; HH = 1.52 mm; HW = 1.82 mm; HID = 2.13 mm; ABVHTP = 128.74 mm3 | 3 | | TSFL = 7.23 kN; HH = 1.44 mm; HW = 2.01 mm; HID = 2.41 mm; ABVHTP = 142.21 mm3 | 4 | | TSFL = 9.46 kN; HH = 1.40 mm; HW = 2.24 mm; HID = 3.209 mm; ABVHTP = 148.45 mm3 | 5 | | TSFL = 8.89 kN; HH = 1.31 mm; HW = 2.10 mm; HID = 2.74 mm; ABVHTP = 142.21 mm3 | 6 | | TSFL = 8.44 kN; HH = 1.52 mm; HW = 1.82 mm; HID = 2.21 mm; ABVHTP = 135.01 mm3 |
|
|