Research Article
Analysis of Turning Performance on AISI O1 Steel Using VO+nMoS2 as Coolant
Table 3
Calculated S/N ratio, normalized S/N ratio, and ASN values.
| Ex. No. | S/N ratio | Normalized S/N ratio (NSN) | ASN | Ra | Vb | T | Fc | Ra | Vb | T | Fc |
| 1 | 4.408 | 33.432 | −38.486 | −50.756 | 0.557 | 1.000 | 0.758 | 0.274 | 0.647 | 2 | 0.593 | 32.956 | −38.890 | −50.423 | 0.250 | 0.884 | 0.669 | 0.357 | 0.540 | 3 | −2.503 | 30.964 | −40.341 | −51.078 | 0.000 | 0.400 | 0.351 | 0.195 | 0.236 | 4 | 3.557 | 31.437 | −40.172 | −50.130 | 0.489 | 0.515 | 0.388 | 0.429 | 0.455 | 5 | 2.338 | 30.516 | −40.424 | −50.857 | 0.390 | 0.291 | 0.333 | 0.249 | 0.316 | 6 | 4.583 | 30.400 | −40.984 | −51.102 | 0.571 | 0.263 | 0.209 | 0.189 | 0.308 | 7 | 4.876 | 31.437 | −41.214 | −49.097 | 0.595 | 0.515 | 0.159 | 0.684 | 0.488 | 8 | 5.288 | 30.574 | −41.656 | −50.553 | 0.628 | 0.305 | 0.062 | 0.324 | 0.330 | 9 | 1.681 | 29.319 | −41.938 | −51.550 | 0.337 | 0.000 | 0.000 | 0.078 | 0.104 | 10 | 4.152 | 33.311 | −38.890 | −49.966 | 0.537 | 0.970 | 0.669 | 0.469 | 0.662 | 11 | 2.047 | 32.217 | −40.000 | −50.264 | 0.367 | 0.704 | 0.426 | 0.396 | 0.473 | 12 | 0.265 | 29.843 | −40.749 | −50.832 | 0.223 | 0.127 | 0.261 | 0.256 | 0.217 | 13 | 2.270 | 32.432 | −39.554 | −50.238 | 0.385 | 0.757 | 0.523 | 0.402 | 0.517 | 14 | 1.210 | 31.213 | −40.588 | −51.866 | 0.299 | 0.460 | 0.297 | 0.000 | 0.264 | 15 | 2.615 | 33.351 | −39.825 | −48.062 | 0.413 | 0.980 | 0.464 | 0.940 | 0.699 | 16 | 6.375 | 32.217 | −40.257 | −48.818 | 0.716 | 0.704 | 0.369 | 0.753 | 0.636 | 17 | 6.936 | 30.873 | −40.424 | −50.130 | 0.761 | 0.378 | 0.333 | 0.429 | 0.475 | 18 | 3.479 | 29.924 | −40.668 | −50.681 | 0.482 | 0.147 | 0.279 | 0.293 | 0.300 | 19 | 6.108 | 33.073 | −38.382 | −51.005 | 0.694 | 0.913 | 0.781 | 0.213 | 0.650 | 20 | 4.959 | 32.841 | −37.385 | −48.850 | 0.602 | 0.856 | 1.000 | 0.745 | 0.801 | 21 | 3.945 | 31.869 | −39.276 | −50.980 | 0.520 | 0.620 | 0.585 | 0.219 | 0.493 | 22 | 7.432 | 32.803 | −39.645 | −48.723 | 0.801 | 0.847 | 0.504 | 0.776 | 0.732 | 23 | 4.365 | 32.217 | −38.588 | −49.426 | 0.554 | 0.704 | 0.736 | 0.603 | 0.654 | 24 | 5.433 | 32.728 | −39.085 | −48.563 | 0.640 | 0.829 | 0.627 | 0.816 | 0.728 | 25 | 7.744 | 32.324 | −40.257 | −47.819 | 0.826 | 0.730 | 0.369 | 1.000 | 0.745 | 26 | 9.897 | 33.432 | −39.825 | −48.399 | 1.000 | 1.000 | 0.464 | 0.857 | 0.830 | 27 | 7.432 | 31.938 | −40.000 | −49.218 | 0.801 | 0.637 | 0.426 | 0.654 | 0.636 |
|
|