Research Article
Corrosion Resistant Coating from Nano Printed Circuit Board Powder for the Reinforced Concrete Structures
Table 3
Comparison of potentiodynamic polarization test.
| S.no | Description | Uncoated rebar | Zinc coated | Nano PCB coated |
| 1 | CAT slope (I/V) | 3.600 | 5.676 | 5.927 | 2 | ANO slope (I/V) | 9.315 | 4.656 | 4.565 | 3 | CAT int (log i) | −3.325 | −3.671 | −3.693 | 4 | ANO int (log i) | −2.870 | −3.545 | −3.613 | 5 | Lin Pol R (ohm) | 37 | 159 | 153 | 6 | CORR I (A) | 9.136e − 0.004 | 2.398e − 0.002 | 2.586e − 0.002 | 7 | Rate (mm/year) | 4.169e + 0.002 | 1.342e + 0.002 | 1.319e + 0.002 | 8 | Rate (Angs/min) | 2.014e + 0.002 | 5.780e + 0.01 | 5.931e + 0.01 | 9 | Rate (gram/h) | 9.518e − 0.004 | 3.012e − 0.002 | 2.96e − 0.002 |
|
|