Investigation of Magnesium and Chromium Fillers FSW Dissimilar Joint of AA6063 and AA 5154
Table 5
Design matrix for tensile strength.
| Experiment particulars | Results | Trial no. | Input factors | Responses | R | W | P | C | M | TS (MPa) |
| 1 | 800 | 90 | 0.05 | 1 | 97.5 : 2.5 | 132 | 2 | 1200 | 150 | 0.2 | 2 | 97.5 : 2.5 | 145 | 3 | 600 | 120 | 0.1 | 1 | 92.5 : 7.5 | 140 | 4 | 1200 | 90 | 0.2 | 3 | 92.5 : 7.5 | 140 | 5 | 800 | 180 | 0.1 | 1 | 92.5 : 7.5 | 139 | 6 | 1000 | 90 | 0.2 | 2 | 97.5 : 2.5 | 144 | 7 | 800 | 150 | 0.25 | 1 | 97.5 : 2.5 | 145 | 8 | 1200 | 90 | 0.2 | 3 | 92.5 : 7.5 | 140 | 9 | 600 | 150 | 0.1 | 3 | 92.5 : 7.5 | 146 | 10 | 1200 | 90 | 0.1 | 3 | 97.5 : 2.5 | 148 | 11 | 1000 | 180 | 0.1 | 3 | 97.5 : 2.5 | 140 | 12 | 1200 | 150 | 0.1 | 4 | 92.5 : 7.5 | 146 | 13 | 800 | 90 | 0.2 | 3 | 97.5 : 2.5 | 139 | 14 | 1200 | 120 | 0.2 | 3 | 92.5 : 7.5 | 140 | 15 | 800 | 150 | 0.2 | 4 | 92.5 : 7.5 | 142 | 16 | 1200 | 150 | 0.2 | 3 | 97.5 : 2.5 | 149 | 17 | 600 | 120 | 0.15 | 2 | 95.0 : 5.0 | 145 | 18 | 1400 | 120 | 0.25 | 2 | 95.0 : 5.0 | 154 | 19 | 1000 | 60 | 0.15 | 2 | 95.0 : 5.0 | 143 | 20 | 1000 | 180 | 0.15 | 2 | 95.0 : 5.0 | 151 | 21 | 1000 | 120 | 0.05 | 2 | 95.0 : 5.0 | 143 | 22 | 1000 | 120 | 0.25 | 2 | 95.0 : 5.0 | 148 | 23 | 1000 | 120 | 0.05 | 0 | 95.0 : 5.0 | 148 | 24 | 1000 | 120 | 0.15 | 4 | 95.0 : 5.0 | 152 | 25 | 1000 | 120 | 0.05 | 2 | 90.0 : 10.0 | 145 | 26 | 1000 | 120 | 0.15 | 4 | 100.0 : 0.0 | 150 | 27 | 1000 | 120 | 0.05 | 2 | 95.0 : 5.0 | 172 | 28 | 1000 | 120 | 0.15 | 2 | 95.0 : 5.0 | 173 | 29 | 1000 | 120 | 0.05 | 4 | 95.0 : 5.0 | 172 | 30 | 1000 | 120 | 0.15 | 2 | 95.0 : 5.0 | 173 | 31 | 1000 | 120 | 0.25 | 4 | 95.0 : 5.0 | 172 | 32 | 1000 | 120 | 0.15 | 2 | 95.0 : 5.0 | 173 |
|
|