Investigation of Magnesium and Chromium Fillers FSW Dissimilar Joint of AA6063 and AA 5154
Table 7
Design matrix for microhardness.
| Experimental details | Results | Trial no. | Input factors | Responses | R | W | P | C | M | MH | (rpm) | (mm/min) | (mm) | (mm) | (%) | (HV) |
| 1 | 600 | 120 | P | C | 97.5 : 2.5 | 68 | 2 | 1200 | 150 | 0.05 | 1 | 97.5 : 2.5 | 70 | 3 | 800 | 90 | 0.2 | 2 | 92.5 : 7.5 | 67 | 4 | 1200 | 150 | 0.1 | 1 | 97.5 : 2.5 | 85 | 5 | 1000 | 180 | 0.2 | 3 | 92.5 : 7.5 | 68 | 6 | 1200 | 90 | 0.1 | 1 | 97.5 : 2.5 | 86 | 7 | 800 | 150 | 0.2 | 2 | 97.5 : 2.5 | 72 | 8 | 1200 | 150 | 0.25 | 1 | 92.5 : 7.5 | 86 | 9 | 1000 | 120 | 0.2 | 3 | 92.5 : 7.5 | 71 | 10 | 1200 | 90 | 0.1 | 3 | 97.5 : 2.5 | 85 | 11 | 1000 | 180 | 0.1 | 3 | 97.5 : 2.5 | 76 | 12 | 1200 | 150 | 0.1 | 3 | 92.5 : 7.5 | 86 | 13 | 800 | 90 | 0.1 | 4 | 97.5 : 2.5 | 75 | 14 | 1200 | 90 | 0.2 | 3 | 92.5 : 7.5 | 88 | 15 | 1000 | 180 | 0.2 | 3 | 92.5 : 7.5 | 74 | 16 | 1200 | 150 | 0.2 | 4 | 97.5 : 2.5 | 87 | 17 | 600 | 120 | 0.2 | 3 | 95.0 : 5.0 | 66 | 18 | 1400 | 150 | 0.15 | 2 | 92.5 : 7.5 | 87 | 19 | 1000 | 60 | 0.25 | 2 | 95.0 : 5.0 | 74 | 20 | 1000 | 150 | 0.15 | 2 | 92.5 : 7.5 | 86 | 21 | 1000 | 120 | 0.15 | 2 | 95.0 : 5.0 | 77 | 22 | 1000 | 120 | 0.05 | 2 | 95.0 : 5.0 | 82 | 23 | 1000 | 120 | 0.25 | 2 | 95.0 : 5.0 | 80 | 24 | 1000 | 120 | 0.05 | 0 | 95.0 : 5.0 | 86 | 25 | 1000 | 120 | 0.15 | 4 | 90.0 : 10.0 | 79 | 26 | 1000 | 120 | 0.05 | 2 | 100.0 : 0.0 | 83 | 27 | 1000 | 120 | 0.15 | 4 | 95.0 : 5.0 | 93 | 28 | 1000 | 120 | 0.05 | 2 | 95.0 : 5.0 | 93 | 29 | 1000 | 120 | 0.15 | 2 | 95.0 : 5.0 | 92 | 30 | 1000 | 120 | 0.05 | 4 | 95.0 : 5.0 | 91 | 31 | 1000 | 120 | 0.15 | 2 | 95.0 : 5.0 | 93 | 32 | 1000 | 120 | 0.25 | 4 | 95.0 : 5.0 | 90 |
|
|