Research Article
Investigation of Magnesium and Chromium Fillers FSW Dissimilar Joint of AA6063 and AA 5154
Table 9
Design matrix for corrosion rate.
| Experimental particulars | Results | Trial no. | Input factors | Responses | R | W | P | C | M | CR | (rpm) | (mm/min) | (mm) | (mm) | (%) | (mm/y) |
| 1 | 800 | 90 | P | C | 97.5 : 2.5 | 5.427 | 2 | 1200 | 90 | 0.05 | 1 | 92.5 : 7.5 | 4.206 | 3 | 800 | 150 | 0.2 | 2 | 92.5 : 7.5 | 3.256 | 4 | 1200 | 150 | 0.1 | 1 | 97.5 : 2.5 | 3.934 | 5 | 800 | 90 | 0.2 | 3 | 92.5 : 7.5 | 3.256 | 6 | 1200 | 90 | 0.1 | 1 | 97.5 : 2.5 | 5.427 | 7 | 800 | 150 | 0.2 | 2 | 97.5 : 2.5 | 3.799 | 8 | 1200 | 150 | 0.25 | 1 | 92.5 : 7.5 | 4.749 | 9 | 800 | 90 | 0.2 | 3 | 92.5 : 7.5 | 5.156 | 10 | 1200 | 90 | 0.1 | 3 | 97.5 : 2.5 | 4.884 | 11 | 800 | 150 | 0.1 | 3 | 97.5 : 2.5 | 4.613 | 12 | 1200 | 150 | 0.1 | 3 | 92.5 : 7.5 | 5.427 | 13 | 800 | 90 | 0.1 | 4 | 97.5 : 2.5 | 4.477 | 14 | 1200 | 90 | 0.2 | 3 | 92.5 : 7.5 | 4.613 | 15 | 800 | 150 | 0.2 | 3 | 92.5 : 7.5 | 3.12 | 16 | 1200 | 150 | 0.2 | 4 | 97.5 : 2.5 | 4.749 | 17 | 600 | 120 | 0.2 | 3 | 95.0 : 5.0 | 4.07 | 18 | 1400 | 120 | 0.15 | 2 | 95.0 : 5.0 | 5.427 | 19 | 1000 | 60 | 0.25 | 2 | 95.0 : 5.0 | 5.563 | 20 | 1000 | 180 | 0.15 | 2 | 95.0 : 5.0 | 3.934 | 21 | 1000 | 120 | 0.15 | 2 | 95.0 : 5.0 | 2.849 | 22 | 1000 | 120 | 0.05 | 2 | 95.0 : 5.0 | 2.442 | 23 | 1000 | 120 | 0.25 | 2 | 95.0 : 5.0 | 2.985 | 24 | 1000 | 120 | 0.05 | 0 | 95.0 : 5.0 | 3.663 | 25 | 1000 | 120 | 0.15 | 4 | 90.0 : 10.0 | 3.256 | 26 | 1000 | 120 | 0.05 | 2 | 100.0 : 0.0 | 4.613 | 27 | 1000 | 120 | 0.15 | 4 | 95.0 : 5.0 | 1.486 | 28 | 1000 | 120 | 0.05 | 2 | 95.0 : 5.0 | 1.085 | 29 | 1000 | 120 | 0.15 | 2 | 95.0 : 5.0 | 0.814 | 30 | 1000 | 120 | 0.05 | 4 | 95.0 : 5.0 | 1.221 | 31 | 1000 | 120 | 0.15 | 2 | 95.0 : 5.0 | 0.949 | 32 | 1000 | 120 | 0.25 | 4 | 95.0 : 5.0 | 1.085 |
|
|