Influence of Drilling Parameters on the Delamination and Surface Roughness of Insulative-Coated Glass/Carbon-Hybrid Composite
Table 3
Experimental sequence followed to drill the HFRP composite samples using full factorial design of experiment.
| Sample no. | Spindle speed (RPM) | Feed rate (mm/rev) | IC thickness (mm) | Delamination (entry) | Delamination (exit) | Surface roughness (μm) |
| 1 | 3000 | 0.02 | 0.5 | 1.080 | 1.086 | 1.75 | 2 | 1.0 | 1.070 | 1.090 | 1.69 | 3 | 1.5 | 1.060 | 1.100 | 1.56 | 4 | 2.0 | 1.020 | 1.160 | 1.47 | 5 | 0.08 | 0.5 | 1.080 | 1.080 | 1.82 | 6 | 1.0 | 1.050 | 1.108 | 1.71 | 7 | 1.5 | 1.068 | 1.078 | 1.52 | 8 | 2.0 | 1.038 | 1.080 | 1.61 |
| 9 | 4500 | 0.02 | 0.5 | 1.080 | 1.100 | 1.63 | 10 | 1.0 | 1.068 | 1.110 | 1.58 | 11 | 1.5 | 1.060 | 1.120 | 1.61 | 12 | 2.0 | 1.050 | 1.158 | 1.42 | 13 | 0.08 | 0.5 | 1.064 | 1.076 | 1.70 | 14 | 1.0 | 1.052 | 1.110 | 1.63 | 15 | 1.5 | 1.062 | 1.102 | 1.62 | 16 | 2.0 | 1.080 | 1.128 | 1.53 |
| 17 | 6000 | 0.02 | 0.5 | 1.052 | 1.116 | 1.41 | 18 | 1.0 | 1.040 | 1.150 | 1.33 | 19 | 1.5 | 1.026 | 1.166 | 1.30 | 20 | 2.0 | 1.140 | 1.206 | 1.35 | 21 | 0.08 | 0.5 | 1.034 | 1.116 | 1.52 | 22 | 1.0 | 1.040 | 1.150 | 1.47 | 23 | 1.5 | 1.026 | 1.160 | 1.46 | 24 | 2.0 | 1.178 | 1.220 | 1.49 |
|
|