Development of New PM Iron-Based Materials for Self-Lubricating Bearings

<table class="table-group" id="tab2"><tr><td><table class="table"><tr><td class="thead-hr" colspan="3"><hr/></td></tr><tr><td align="left" rowspan="3">Sintering conditions</td><td align="left">Sintering temperature [°C]</td><td align="center">800–900</td></tr><tr><td align="left">Holding time [min.]</td><td align="center">20, 35, 50</td></tr><tr><td align="left">Atmosphere</td><td align="center">Dry hydrogen</td></tr><tr><td align="center" colspan="3"><hr/></td></tr><tr><td align="left">Sintered density [g/cm<sup>3</sup>]</td><td align="left"></td><td align="center">6.5–6.9</td></tr><tr class="table-tr"><td colspan="3"><hr class="tbody-hr"/></td></tr></table></td></tr></table>

Advances in Tribology

tab2

Table 2

Table 2: Development of New PM Iron-Based Materials for Self-Lubricating Bearings 