Studies on Erosion Behavior of Plasma Sprayed Coatings of Glass Microspheres Premixed with Al2O3 Particles
Table 6
Experimental design using L16 orthogonal array and the wear test results.
| A Impact velocity (m s−1) | B Impingement angle (degree) | C Erodent size (µm) | D Erodent temperature (°C) | E Alumina content (wt%) | Erosion rate (mg kg−1) | S/N ratio (db) |
| 32 | 30 | 50 | 30 | 0 | 8.56667 | −18.6562 | 32 | 45 | 100 | 60 | 10 | 11.65643 | −21.3313 | 32 | 60 | 150 | 90 | 20 | 14.23695 | −23.0683 | 32 | 90 | 200 | 120 | 30 | 17. 04751 | −24.6332 | 40 | 30 | 100 | 90 | 30 | 13.34126 | −22.5039 | 40 | 45 | 50 | 120 | 20 | 15.56129 | −23.8409 | 40 | 60 | 200 | 30 | 10 | 20.98768 | −26.4393 | 40 | 90 | 150 | 60 | 0 | 18.81183 | −25.4886 | 48 | 30 | 150 | 120 | 10 | 16.23178 | −24.2073 | 48 | 45 | 200 | 90 | 0 | 16.53376 | −24.3674 | 48 | 60 | 50 | 60 | 30 | 17.43003 | −24.8260 | 48 | 90 | 100 | 30 | 20 | 20.46321 | −26.2195 | 56 | 30 | 200 | 60 | 20 | 19.00984 | −25.5796 | 56 | 45 | 150 | 30 | 30 | 19.14336 | −25.6404 | 56 | 60 | 100 | 120 | 0 | 20.44331 | −26.2110 | 56 | 90 | 50 | 90 | 10 | 22.27585 | −26.9567 |
|
|