Research Article
Process Optimization and Wear Behavior of Red Mud Reinforced Aluminum Composites
Table 2
Grey relational analysis.
| S. number | ratio (dB) | Data preprocessing | Grey relational coefficient | Grey relational grade | Order | Specific wear rate | COF | Specific wear rate | COF | Specific wear rate | COF |
| 1 | −10.542 | 6.213823 | 0.50627 | 0.62920 | 0.660332 | 0.063161 | 0.723493 | 20 | 2 | −15.944 | 8.754143 | 0.612864 | 0.30747 | 0.736494 | 0.04612 | 0.782614 | 15 | 3 | −18.3153 | 11.18182 | 0.659657 | 0 | 0.775772 | 0.036667 | 0.812439 | 13 | 4 | −18.0558 | 4.761443 | 0.654537 | 0.81315 | 0.771272 | 0.080076 | 0.851348 | 11 | 5 | −22.4217 | 8.290785 | 0.740688 | 0.36615 | 0.854708 | 0.048508 | 0.903216 | 5 | 6 | −23.6591 | 8.971 | 0.765104 | 0.28000 | 0.881742 | 0.045082 | 0.926824 | 2 | 7 | −12.6065 | 10.11691 | 0.547008 | 0.13487 | 0.687503 | 0.040289 | 0.727792 | 19 | 8 | −22.6497 | 8.134279 | 0.745186 | 0.38597 | 0.859563 | 0.049371 | 0.908934 | 4 | 9 | −21.0531 | 10.60356 | 0.713681 | 0.07323 | 0.826674 | 0.038549 | 0.865222 | 9 | 10 | −1.86143 | 3.999413 | 0.334979 | 0.90966 | 0.566237 | 0.093168 | 0.659405 | 24 | 11 | −3.86249 | 4.222498 | 0.374465 | 0.88141 | 0.585469 | 0.088912 | 0.674381 | 22 | 12 | −14.8413 | 10.03379 | 0.591106 | 0.14540 | 0.719553 | 0.040602 | 0.760156 | 18 | 13 | −1.01223 | 3.286189 | 0.318222 | 1 | 0.558452 | 0.11 | 0.668452 | 23 | 14 | −23.6705 | 7.9588 | 0.76533 | 0.40820 | 0.882 | 0.050376 | 0.932376 | 1 | 15 | −20.4813 | 5.005274 | 0.702399 | 0.78227 | 0.815499 | 0.076631 | 0.89213 | 6 | 16 | −17.3482 | 7.618133 | 0.640573 | 0.45134 | 0.759258 | 0.052448 | 0.811706 | 14 | 17 | −18.4535 | 5.596814 | 0.662384 | 0.70735 | 0.778191 | 0.069388 | 0.847578 | 12 | 18 | −14.385 | 8.268254 | 0.582101 | 0.36901 | 0.712768 | 0.04863 | 0.761398 | 16 | 19 | 18.86953 | 3.661923 | −0.0741 | 0.95241 | 0.422467 | 0.100441 | 0.522908 | 27 | 20 | 13.35527 | 4.436975 | 0.034713 | 0.85425 | 0.453065 | 0.085172 | 0.538238 | 26 | 21 | −20.0999 | 8.068058 | 0.694872 | 0.39436 | 0.808211 | 0.049745 | 0.857956 | 10 | 22 | 0.063815 | 4.222498 | 0.296989 | 0.88141 | 0.54889 | 0.088912 | 0.637802 | 25 | 23 | −20.2203 | 6.70716 | 0.697248 | 0.56672 | 0.810497 | 0.058932 | 0.86943 | 8 | 24 | −22.7325 | 7.937113 | 0.74682 | 0.41095 | 0.861341 | 0.050503 | 0.911844 | 3 | 25 | −10.2883 | 7.432221 | 0.501263 | 0.47489 | 0.65714 | 0.053653 | 0.710793 | 21 | 26 | −21.0146 | 8.290785 | 0.71292 | 0.36615 | 0.82591 | 0.048508 | 0.874418 | 7 | 27 | −14.5979 | 9.093858 | 0.586302 | 0.26444 | 0.715918 | 0.044514 | 0.760432 | 17 |
|
|