Effect of Tungsten Carbides on Abrasive Wear of Hardfacing Coatings
Table 5
Results from tribometry, in mm3 volume loss.
| Series | No. 1 | No. 2 | No. 3 | No. 4 | No. 5 | No. 6 | No. 7 | No. 8 | Base | Fe | Fe | Ni | Fe | Ni | Ni | Fe | Fe |
| Volume loss after 3000 rotations (Steel-Wheel) | mm3 |
| Mean | 151.3 | 122.6 | 304.1 | 543.0 | 426.8 | 412.4 | 20.7 | 57.3 | STD | 80.3 | 44.5 | 162.2 | 210.5 | 186.9 | 226.8 | 9.6 | 27.8 |
| Volume loss after 6000 rotations (Steel-Wheel) | mm3 |
| Mean | 332.8 | 321.7 | 514.3 | 785.0 | 624.2 | 614.6 | 44.6 | 106.2 | STD | 201.5 | 77.9 | 231.6 | 277.1 | 173.7 | 266.0 | 13.8 | 44.7 |
| Volume loss after 3000 rotations (Rubber-Wheel) | mm3 |
| Mean | 853.5 | 549.9 | 208.1 | 263.3 | 116.8 | 133.8 | Not tested | STD | 193.1 | 122.4 | 7.4 | 40.5 | 35.1 | 62.8 |
| Volume loss after 6000 rotations (Rubber-Wheel) | mm3 |
| Mean | 1479.8 | 1057.3 | 386.4 | 422.5 | 199.6 | 310.0 | Not tested | STD | 363.5 | 226.4 | 46.9 | 80.6 | 49.5 | 79.6 |
|
|