Wear Resistance of (Diamond-Ni)-Ti6Al4V Gradient Materials Prepared by Combined Selective Laser Melting and Spark Plasma Sintering Techniques
Figure 9
Volumetric wear rate (missing volume) of samples during impact-abrasive test measured by 3D OSP, ×103 μm3.