Effect of Load on the Tribological Properties of Eutectic Al-Si Reinforced n-Al2O3 under Dry Sliding Conditions
Table 1
Theoretical density, practical density, and porosity content comparison for different composition samples.
| Composition | Reinforcement wt. % | Theoretical density (g/cm3) | Practical density (g/cm3) | Density (%) | Porosity content (vol. %) |
| Base composition | Al-Si | 2.66 | 2.65 | 99.62 | 0.3759 | Composition 1 | Al-Si + 2 wt.% Al2O3 | 2.68 | 2.654 | 99.02 | 0.9701 | Composition 2 | Al-Si + 4 wt.% Al2O3 | 2.712 | 2.666 | 98.30 | 1.696 | Composition 3 | Al-Si + 6 wt.% Al2O3 | 2.737 | 2.691 | 98.31 | 1.680 | Composition 4 | Al-Si + 8 wt.% Al2O3 | 2.763 | 2.7 | 97.71 | 2.280 | Composition 5 | Al-Si + 10 wt.% Al2O3 | 2.789 | 2.51 | 89.99 | 10.003 |
|
|