Characterization and Optimization of Mechanical Properties of ABS Parts Manufactured by the Fused Deposition Modelling Process
Table 3
Input process parameters that affect output responses.
| Run | layer thickness | part orientation | raster angle | raster width | air gap | Measured (MPa) | Predicted (MPa) |
| 1 | 0.127 | 0 | 0 | 0.2032 | −0.00254 | 32.56 | 27.76 | 2 | 0.127 | 0 | 0 | 0.2032 | 0.5588 | 6.52 | 4.74 | 3 | 0.127 | 0 | 0 | 0.5588 | −0.00254 | 24.81 | 28.14 | 4 | 0.127 | 0 | 0 | 0.5588 | 0.5588 | 10.44 | 8.58 | 5 | 0.127 | 0 | 45 | 0.2032 | −0.00254 | 34.61 | 30.96 | 6 | 0.127 | 0 | 45 | 0.2032 | 0.5588 | 4.78 | 4.39 | 7 | 0.127 | 0 | 45 | 0.5588 | −0.00254 | 30.15 | 31.96 | 8 | 0.127 | 0 | 45 | 0.5588 | 0.5588 | 8.08 | 8.84 | 9 | 0.127 | 90 | 0 | 0.2032 | −0.00254 | 12.86 | 12.60 | 10 | 0.127 | 90 | 0 | 0.2032 | 0.5588 | 4.39 | 5.10 | 11 | 0.127 | 90 | 0 | 0.5588 | −0.00254 | 23.55 | 23.89 | 12 | 0.127 | 90 | 0 | 0.5588 | 0.5588 | 9.56 | 8.58 | 13 | 0.127 | 90 | 45 | 0.2032 | −0.00254 | 15.1 | 14.33 | 14 | 0.127 | 90 | 45 | 0.2032 | 0.5588 | 4.01 | 4.96 | 15 | 0.127 | 90 | 45 | 0.5588 | −0.00254 | 24.3 | 26.67 | 16 | 0.127 | 90 | 45 | 0.5588 | 0.5588 | 8.09 | 8.78 | 17 | 0.3302 | 0 | 0 | 0.4572 | −0.00254 | 31.46 | 28.32 | 18 | 0.3302 | 0 | 0 | 0.4572 | 0.9652 | 8.43 | 9.19 | 19 | 0.3302 | 0 | 0 | 0.9652 | −0.00254 | 24.99 | 25.85 | 20 | 0.3302 | 0 | 0 | 0.9652 | 0.9652 | 9.39 | 11.35 | 21 | 0.3302 | 0 | 45 | 0.4572 | −0.00254 | 31.42 | 32.05 | 22 | 0.3302 | 0 | 45 | 0.4572 | 0.9652 | 7.12 | 9.06 | 23 | 0.3302 | 0 | 45 | 0.9652 | −0.00254 | 28.94 | 29.42 | 24 | 0.3302 | 0 | 45 | 0.9652 | 0.9652 | 11.07 | 10.96 | 25 | 0.3302 | 90 | 0 | 0.4572 | −0.00254 | 20.55 | 22.30 | 26 | 0.3302 | 90 | 0 | 0.4572 | 0.9652 | 8.89 | 8.64 | 27 | 0.3302 | 90 | 0 | 0.9652 | −0.00254 | 24.72 | 25.14 | 28 | 0.3302 | 90 | 0 | 0.9652 | 0.9652 | 11.28 | 10.53 | 29 | 0.3302 | 90 | 45 | 0.4572 | −0.00254 | 24.96 | 24.92 | 30 | 0.3302 | 90 | 45 | 0.4572 | 0.9652 | 8.82 | 8.58 | 31 | 0.3302 | 90 | 45 | 0.9652 | −0.00254 | 27.35 | 27.85 | 32 | 0.3302 | 90 | 45 | 0.9652 | 0.9652 | 11.63 | 10.34 |
|
|