Corrosion and Corrosion Inhibition of High Strength Low Alloy Steel in 2.0 M Sulfuric Acid Solutions by 3-Amino-1,2,3-triazole as a Corrosion Inhibitor
Figure 2
SEM micrographs obtained for the HSLA steel after 24 h immersion in 2.0 M H2SO4 solutions, (a) without ATA and (b) with 5.0 mM ATA present, and (c) EDS profile analysis corresponding to the surface shown in Figure 2(b), respectively.