| Catalysts | Conditions | , min-1 | References |
| TiO2 TiO2-boron nitride nanocomposite | g L-1, mg L-1, , UV light irradiation, min | 0.047 0.054 | [10] | Fe-zeolite catalyst (of ZSM5 type) | g L-1, mM, , mg L-1, °C, min | 0.014 | [23] | Recycled rusted iron particles | g L-1, mM, , μg L-1, °C, min | 0.140 | [35] | Zeolite-TiO2-UV/ultrasound/H2O2 | g L-1, mM, , °C, min, W | 0.031 | [36] | Ultrasound/BaTiO3 nanowires/piezoelectric catalytic persulfate | g L-1, mM, mg L-1, min | 0.082 | [37] | Co3O4 : Bi (1 : 2) nanocomposite | g L-1, mg L-1, , °C, min, visible light irradiation | 0.094 | [38] | TiO2/UV g-C3N4/Vis | g L-1, μg L-1, , °C, min, W g L-1, μg L-1, , °C, min, W | 1.000 0.030 | [39] | FeOx-MnOx/SBA-15 | g L-1, mM, μg L-1, , °C, min | 0.032 | [40] | 10 wt% g-C3N4/MIL-68(In)-NH2 | g L-1, mg L-1, , °C, min, W | 0.017 | [41] | MgFe2O4 | g L-1, mM, mg L-1, , °C, min | 0.091 | This study |
|
|