Research Article
Model Building and Optimization Analysis of MDF Continuous Hot-Pressing Process by Neural Network
Table 4
Experimental data set in MDF hot-pressing.
| No. | TE (°C) | PR (MPa) | TI (min) | MC (%) | MOR (Mpa) | MOE (MPa) | IB (Mpa) |
| 1 | 170 | 3 | 4 | 8 | 25.66 | 2538.93 | 0.4775 | 2 | 170 | 3.4 | 5 | 10 | 29.1275 | 2887.788 | 0.62 | 3 | 170 | 2.7 | 6 | 12 | 33.95 | 3159.645 | 0.635 | 4 | 180 | 3 | 6 | 10 | 29.9025 | 2967.803 | 0.625 | 5 | 180 | 3.4 | 4 | 12 | 31.76 | 3034.485 | 0.7025 | 6 | 180 | 2.7 | 5 | 8 | 33.1925 | 3215.603 | 0.5625 | 7 | 190 | 3 | 5 | 12 | 33.98 | 3122.16 | 0.72 | 8 | 190 | 3.4 | 6 | 8 | 35.1575 | 3191.608 | 0.63 | 9 | 190 | 2.7 | 4 | 10 | 31.955 | 3034.818 | 0.65 | 10 | 180 | 3 | 4 | 8 | 25.13 | 2296.26 | 0.42 | 11 | 170 | 3.4 | 4 | 10 | 20.36 | 2601.56 | 0.5 | 12 | 170 | 2.7 | 4 | 12 | 28 | 2743.05 | 0.44 | 13 | 190 | 3 | 4 | 12 | 35.74 | 3063.48 | 0.687 | 14 | 180 | 3.4 | 4 | 8 | 22.2025 | 2707.743 | 0.7 | 15 | 190 | 2.7 | 5 | 10 | 30.85 | 3212.7 | 0.68 | 16 | 190 | 3 | 6 | 12 | 32.65 | 2982.33 | 0.66 | 17 | 170 | 3.4 | 6 | 10 | 29.38 | 3487.39 | 0.77 | 18 | 180 | 2.7 | 4 | 8 | 25.87 | 2304.19 | 0.41 | 19 | 190 | 2.7 | 6 | 10 | 27.63 | 2539.05 | 0.49 | 20 | 180 | 2.7 | 5 | 10 | 28.35 | 2675.37 | 0.42 | 21 | 170 | 2.7 | 5 | 8 | 14.63 | 1806.99 | 0.5431 | 22 | 180 | 3 | 5 | 12 | 34.52 | 3462.12 | 0.63 | 23 | 190 | 3.4 | 5 | 10 | 38.07 | 3457.79 | 0.77 |
|
|