Critical Analysis on the Structural and Magnetic Properties of Bulk and Nanocrystalline Cu-Fe-O
Figure 11
Increase in magnetization () as a function of % of “Fe” in CuO at 300 K for the 50-hour refluxed nanocrystalline sample annealed at 900°C/2h in air. Inset shows the comparison with pure copper ferrite.