Research Article
Use of Sawing Waste from Zeolitic Tuffs in the Manufacture of Ceramics
Table 4
Weight loss (
%) and linear shrinkage (
%) of compacts arising from various thermal treatments.
(a) Thermal treatments summarised in Table 1b |
| | Cab70 | LacBen | T() | % | % | % | % |
| 500 | 8.2 | 0.4 | 8.8 | 1.8 | 700 | 11.4 | 1.3 | 11.5 | 3.2 | 800 | 12.7 | 2.8 | 13.9 | 3.5 | 900 | 12.8 | 3.9 | 14.2 | 4.7 | 1000 | 14.9 | 5.5 | 14.5 | 15.9 | 1200 | melting | – | melting | – |
|
|
(b) Thermal treatments summarised in Table 1c |
| | Cab70 | LacBen | T () | % | % | % | % |
| 1050 | 13.0 | 25.3 | 14.5 | 25.5 |
|
|
(c) Thermal treatments summarised in Table 1d and 1e |
| | Cab70 | LacBen | T () | % | % | % | % |
| 1050 (see Table 3d) | 12.9 | 25.7 | | | 1100 (see Table 3e) | partial melting | 14.3 | 24.7 |
|
|
(d) Thermal treatments summarised in Table 1f and 1g (h = 3 cm) |
| | Cab70 | LacBen | T () | % | % | % | % |
| 1050 (see Table 3f) | 13.0 | 17.5 | | | 1100 (see Table 3g) | | | 14.6 | 19.2 |
|
|
(e) Thermal treatments summarised in Table 1h, 1i, 1l and 1m |
| | Cab70 | LacBen | T () | % | % | % | % |
| 1050 (see Table 3h) | 4.9 | 16.2 | | | 1100 (see Table 3i) | | | 2.3 | 16.9 | 1050 (see Table 3l) | 9.0 | 16.7 | | | 1100 (see Table 3m) | | | 6.0 | 17.4 |
|
|