Review Article
Strengthening Mechanisms of Magnesium-Lithium Based Alloys and Composites
Figure 9
Micrograph of LAZ1151: (a) 30% cold rolling, average grain size ~227 μm, (b) 60% cold rolling, average grain size ~171 μm, and (c) 90% cold rolling, average grain size ~147 μm [11].