Microstructural Changes during High Temperature Service of a Cobalt-Based Superalloy First Stage Nozzle
Figure 1
Blade root micrograph of (a) gamma prime () without degradation and (b) gamma prime () with moderate degradation after 24000 h in service, IN738LC superalloy.