Experimental Investigation and FE Analysis on Constitutive Relationship of High Strength Aluminum Alloy under Cyclic Loading
Table 3
Test results of cyclic loading.
| Specimen | /MPa | /MPa | /MPa | /% | | /kN⋅mm |
| H1 | 545.14 | | | 0.94 | 6 | 185.68 | H2 | 543.56 | 615.99 | 594.53 | 0.90 | 10 | 77.75 | H3 | 544.18 | 606.12 | 598.96 | 0.94 | 6 | 53.80 | H4 | 542.66 | 627.07 | 597.42 | 0.95 | 6 | 117.26 | H5 | 542.08 | 631.12 | 602.66 | 0.88 | 5 | 113.75 | H6 | 548.83 | 604.14 | 604.03 | 0.89 | 5 | 116.57 | H7 | 543.27 | 619.57 | 593.52 | 0.95 | 6 | 55.68 | H8 | 530.48 | 613.02 | 587.04 | 0.87 | 6 | 55.57 | H9 | 541.29 | 605.20 | 601.27 | 0.90 | 5 | 112.44 | H10 | 544.15 | 618.60 | 592.09 | 0.84 | 5 | 59.52 | H11 | 532.39 | 599.03 | 580.14 | 0.98 | 6 | 61.24 | H12 | 542.88 | 615.72 | 590.75 | 0.87 | 7 | 95.67 | H13 | 542.89 | 623.28 | 595.65 | 0.91 | 5 | 121.96 | H14 | 550.99 | 628.30 | 613.66 | 0.93 | 6 | 173.97 | H15 | 554.52 | 612.95 | 599.64 | 1.00 | 5 | 23.17 |
|
|