Influence of Nano-SiO2 on the Consistency, Setting Time, Early-Age Strength, and Shrinkage of Composite Cement Pastes
Table 3
Setting time and early-age compressive strength of cement pastes.
| Serial number | Setting time | Compressive strength (MPa) | Initial | Final | Time difference | 1 d | 3 d | 7 d |
| 0# | 8 hr 15 min | 9 hr 20 min | 1 hr 5 min | 12.3 | 27.1 | 34.0 | A1 | 8 hr 10 min | 9 hr 10 min | 1 hr | 13.0 | 28.4 | 36.7 | A2 | 6 hr 50 min | 8 hr 5 min | 1 h 15 min | 14.5 | 31.3 | 40.1 | A3 | 6 hr 35 min | 7 hr 55 min | 1 h 20 min | 15.2 | 35.4 | 45.0 | B1 | 5 hr 50 min | 7 hr 20 min | 1 h 30 min | 15.3 | 36.0 | 45.4 | B2 | 5 hr 25 min | 7 hr 15 min | 1 hr 50 min | 16.7 | 38.2 | 47.2 | B3 | 4 hr 50 min | 6 hr 45 min | 1 hr 55 min | 16.0 | 39.4 | 47.5 | C1 | 9 hr 10 min | 10 hr 20 min | 1 hr 10 min | 6.7 | 14.5 | 28.4 | C2 | 7 hr 40 min | 9 hr | 1 hr 20 min | 10.8 | 28.7 | 38.6 | C3 | 6 hr 15 min | 7 hr 45 min | 1 hr 30 min | 14.0 | 32.5 | 41.7 |
|
|