Processing and Quality Evaluation of Additive Manufacturing Monolayer Specimens
Table 1
Strength and modulus comparison.
| | Specimen type | Test speed [mm/min] | Modulus [MPa] | Strength [MPa] | Elongation at break [%] |
| Tensile | Filament | 2 | 2060 ± 633 | 51.4 ± 0.9 | 17.2 ± 8.4 | Monolayer | 2 | 2180 ± 54 | 47.0 ± 0.6 | 5.1 ± 2.2 | PLA [17] | >12.5 | 3500 | 53 | 6.0 |
| Compression | Monolayer | 2 | 1896 ± 45 | 58.2 ± 1.1 | n.a. | PLA [18] | 0.34 | 2300 | 108 | n.a. |
|
|