Al6061 Hybrid Metal Matrix Composite Reinforced with Alumina and Molybdenum Disulphide
Table 11
Experimental result of surface roughness for Al6061/12 wt.% Al2O3/6 wt.% MoS2.
| Trial | V | F | D | V | F | D | Ra (μm) | S/N ratio |
| 1 | 1 | 1 | 1 | 100 | 0.1 | 1 | 2.21 | −6.887 | 2 | 1 | 2 | 2 | 100 | 0.2 | 1.5 | 2.35 | −7.421 | 3 | 1 | 3 | 3 | 100 | 0.3 | 2 | 3.56 | −11.029 | 4 | 2 | 1 | 2 | 150 | 0.1 | 1.5 | 2.48 | −7.889 | 5 | 2 | 2 | 3 | 150 | 0.2 | 2 | 2.65 | −8.464 | 6 | 2 | 3 | 1 | 150 | 0.3 | 1 | 3.62 | −11.174 | 7 | 3 | 1 | 3 | 200 | 0.1 | 2 | 2.88 | −9.187 | 8 | 3 | 2 | 1 | 200 | 0.2 | 1 | 3.02 | −9.600 | 9 | 3 | 3 | 2 | 200 | 0.3 | 1.5 | 3.87 | −11.754 |
|
|