On the Development of an Al4.8 wt% Cu Alloy Obtained from Recycled Aluminum Cans Designed for Thixoforming Process
Table 2
Results of the tensile tests.
| | 2024 [14] | Can alloy | Al4.8 wt% Cu | Thixoforged – Al4.8 wt% Cu | (T6) | (F) | (T6) | = 0.6, 615°C (T6) | = 0.8, 580°C (T6) | 20 min | 30 min | 20 min | 30 min |
| (MPa) | 345 | 111 | 207 ± 30 | 257 ± 18 | 202 ± 18 | 200 ± 12 | 222 ± 9 | (MPa) | 425 | 151 | 307 ± 19 | 324 ± 10 | 282 ± 9 | 283 ± 6 | 331 ± 4 | (%) | 10 | 6.2 | 4.5 ± 1 | 7.1 ± 1 | 9.0 ± 1 | 5.3 ± 2 | 7.8 ± 2 |
|
|
Yield strength. Ultimate strength. Elongation. F (as cast). T6 (solutionizing during 24 h at 525°C and aging during 3 h at 190°C).
|