Influence of Inertia and Low Active Mineral Admixture on Strength and Microstructure of Cement-Based Materials

Table 5

CH content of the hydration products/mass, %.

Sample	Seven days	90 days
C	13.46	16.39
L2	13.36	14.81
R2	12.53	11.35
G2	12.18	11.04
L4	12.01	10.88
R4	11.98	10.65
G4	9.59	9.37
L6	4.13	3.99
R6	2.92	0.85
G6	1.23	0.00